Shrinkage vs. Shrinkage Stress: What Does it Mean for Your Composite?

Shrinkage

Just like a wool sweater shrinking in a hot dryer, composites will shrink during polymerization. This is the process whereby simple molecules called monomers combine to form larger, more complex molecules, or polymers. Depending on the monomers combined, the resulting product can have any number of unique physical properties, including strength or elasticity. However, polymerization can also have some unavoidable adverse outcomes.

For restorative composites, when the resin converts from a semi-liquid or paste to a solid, its density changes along with its overall volume – literally decreasing in size. Conventional materials shrink by about 1.5-5% during curing.

Shrinkage Stress

Imagine you’ve accidentally shrunk your favorite wool sweater. What would happen if you decided to keep wearing it? Beyond being uncomfortable and tight, the tiny sweater would take up less space physically – leaving gaps at your wrists, waist and in your closet.

That’s the fundamental difference between shrinkage and shrinkage stress. On its own, the shrunken sweater or polymerized composite is smaller and takes up less space – but on your body and in a cavity, it can cause a lot of discomfort. Shrinkage causes shrinkage stress, but they aren’t the same thing.

Shrinkage stress is the pressure put on the adhesive and surrounding tooth structure during the polymerization process. If this pressure exceeds the adhesive bond, or the strength of either the composite or tooth, it can cause a variety of problems, such as:

Debonding resulting in internal or marginal gaps

Fractures in the material and/or tooth structure

Marginal staining

Microleakage

Secondary caries

Postoperative sensitivity^1-4

Why knowing the difference matters

Composite resins will undergo some degree of volumetric shrinkage no matter what you do – but that doesn’t necessarily mean it has to impact the success of the restoration. Just as different clothing materials will react differently to a hot dryer, different composites experience shrinkage and stress differently.

Imagine you threw a pair of wool pants and a pair of spandex tights into a hot dryer and both items shrank the same amount. Which do you think would be more uncomfortable to try on? Because of the properties of the material, the spandex would stretch and put less stress on the body, while the stiffness of the wool pants would make them less forgiving and likely to burst at the seams. Similarly, flowable composites may shrink the same amount as a universal (or even more), but their low elastic modulus relieves polymerization stress.

That’s why it’s so important to not only know the difference between shrinkage and shrinkage stress, but also to pay attention to the properties of your composite. Selecting a low-shrinkage composite doesn’t necessarily guarantee less stress, just as buying pre-shrunk wool won’t guarantee a comfortable fit.

How to Cope

While polymerization shrinkage can’t be eliminated completely, there are a number of ways to reduce stress. However, many of these strategies, from layering to soft-start curing, are dependent on the properties of the composite.^1-3Traditional universal composites, for instance, require incremental placement to reduce shrinkage and stress – but this technique can also increase the potential for voids, poor adaptation and contamination from blood or saliva. Ultimately, reducing shrinkage stress comes down to choosing the right material, which should in turn simplify placement and cavity prep. For example, a modern bulk fill, such as 3M™ Filtek™ One Bulk Fill Restorative, eliminates the need for layering techniques and enables one-step placement because of its low-stress monomers and high depth of cure.

Conclusion

When performing composite restorations, polymerization shrinkage and shrinkage stress are inevitable – but they aren’t insurmountable obstacles. The more you know about how each impacts the tooth and success of the restoration, the better prepared you’ll be to find the best fit for each case.